Laser cladding of quasicrystal forming Al–Cu–Fe on aluminum

Biswas, Krishanu and Galun, Rolf and Mordike, Barry L and Chattopadhyay, Kamanio (2004) Laser cladding of quasicrystal forming Al–Cu–Fe on aluminum. In: Journal of Non-Crystalline Solids, 334-33 . pp. 517-523.

[img] PDF
Laser_cladding_Feb26th.pdf
Restricted to Registered users only

Download (839Kb) | Request a copy

Abstract

Composite quasicrystalline coatings are developed by laser cladding of an elemental powder mixture of aluminum, copper and iron on an aluminum substrate. Some of the tracks are remelted to see the effect of phase formation and related changes in hardness during remelting. The clad layers start growing with a cellular morphology from the substrate. The icosahedral phase forms in all the tracks along with some aluminides. It has also been found that the icosahedral phase forms both by a peritectic reaction between the liquid and $Al_{13}Fe_4$ and by direct nucleation from the liquid. This is a clear indication of a different levels of undercooling that the liquid undergoes before the nucleation of the primary phase inside the clad layers during laser processing. The formation of $Al_{13}Fe_4$ with a ten-pointed star like morphology has also been found at the bottom of the clad. The remelting of the clad tracks leads to a change in microstructure as far as phase formation is concerned. The formation of long lath-shaped $Al_{13}Fe_4$ can be observed in the remelted layer. The hardness profiles of the clad and remelted layers reveal a hardness $(HV_{0.025})$ around 600.

Item Type: Journal Article
Additional Information: Copyright of this article belongs to Elsevier.
Department/Centre: Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 30 Nov 2007
Last Modified: 19 Sep 2010 04:36
URI: http://eprints.iisc.ernet.in/id/eprint/10133

Actions (login required)

View Item View Item