Synthesis and characterization of calcium containing poly(urethane-ether)s

Prasath, Arun R and Nanjundan, S and Pakula, T and Klapper, M (2004) Synthesis and characterization of calcium containing poly(urethane-ether)s. In: European Polymer Journal, 40 (8). pp. 1767-1778.

[img] PDF
synthesis.pdf - Published Version
Restricted to Registered users only

Download (464Kb) | Request a copy
Official URL: http://dx.doi.org/10.1016/j.eurpolymj.2004.03.007

Abstract

Calcium containing poly(urethane-ether)s (PUEs) were synthesized by the reaction of hexamethylene diisocyanate or toluylene 2,4-diisocyanate (HMDI or TDI) with a mixture of calcium salt of mono(hydroxybutyl)phthalate $[Ca(HBP)_2]$ and polyethylene glycol ($PEG_2_0_0$ or $PEG_4_0_0$). A series of calcium containing PUEs having different composition were synthesized by taking the mole ratio of $Ca(HBP)_2$:$PEG_2_0_0$ or $PEG_4_0_0$:diisocyanate (HMDI or TDI) as 3:1:4, 2:2:4 and 1:3:4 to study the effect of calcium content on the properties of the copolymer. The structure of the polymers were confirmed by IR, $^1H-NMR,$ $^13C-NMR,$ and solid state $^13C-CP-MAS$ NMR. The polymers were soluble in dimethyl sulfoxide and dimethyl formamide. The initial decomposition temperature of the polymers decreases with increase in calcium content. The $T_g$ value of PUEs increases with increase in calcium content and decreases with increase in soft segment content and length. A single $T_g$ value is observed for the calcium containing PUEs based on $PEG_2_0_0$ shows the presence of homogeneous phase. However, two $T_g$ values for the PUEs based on $PEG_4_0_0$ for various composition of $Ca(HBP)_2$, $PEG_4_0_0$ and diisocyanate (HMDI or TDI) shows the presence of heterogeneous phase. The viscosity of the calcium containing PUEs increases with increase in the soft segment content as well as its length and decreases with increase in calcium content. X-ray diffraction patterns of the polymers show that the HMDI based polymers are partially crystalline and TDI based polymers are amorphous in nature. The dynamic mechanical analysis of the calcium containing PUEs based on HMDI shows that at any given temperature modulus $(g^' and g^")$ increases with increase in the ionic content in the polymers.

Item Type: Journal Article
Additional Information: This article copyright belongs to Elsevier Science.
Keywords: Calcium salt of mono(hydroxybutyl)phthalate;Polyethylene glycol;Poly(urethane-ether)s;Spectral studies;Thermal studies;Visco-elastic properties
Department/Centre: Division of Chemical Sciences > Inorganic & Physical Chemistry
Date Deposited: 26 Jun 2007
Last Modified: 16 Jan 2012 05:03
URI: http://eprints.iisc.ernet.in/id/eprint/11224

Actions (login required)

View Item View Item