Structral, thermal and electrical properties of $CrSi_2$

Dasgupta, T and Etourneau, J and Chevalier, B and Matar, SF and Umarji, AM (2008) Structral, thermal and electrical properties of $CrSi_2$. In: Journal of Applied Physics, 103 (11). pp. 113516-1.

[img] PDF
fulltext.pdf
Restricted to Registered users only

Download (799Kb) | Request a copy

Abstract

Stoichiometric $CrSi_2$ was prepared by arc melting and compacted by uniaxial hot pressing for property measurements. The crystal structure of $Cr_Si_2$ was investigated using the powder x-ray diffraction method. From the Rietveld refinement, the lattice parameters were found to be a =4.427 57 (7) and c=6.368 04 (11) \AA, respectively. The thermal expansion measurement revealed an anisotropic expansion in the temperature range from room temperature 800K with $\alpha_a$ = 14.58 \times $10^{-6}/K$, $\alpha_c$ = 7.51 \times $10^{-6}/K$ and $\alpha_v$ = 12.05 \times $10^{-6}/K$.The volumetric thermal expansion coefficient shows an anomalous decrease in the temperature range of 450-600 K. The measured electrical resitivity and thermoelectric power S have similar trends with a maxima around 550K. Thermal conductivity meaurements show a monotonic decrease with increasing temperature from a room temperature value of 10 W $m^{-1} K^{-1}$.The ZT values incrase with temperature and have a maximum value of 0.18 in the temperature range studied.An analysis of the electronic band structure is provided.

Item Type: Journal Article
Additional Information: Copyright of this article belongs to American Institute of Physics.
Department/Centre: Division of Chemical Sciences > Materials Research Centre
Date Deposited: 11 Jul 2008
Last Modified: 19 Sep 2010 04:47
URI: http://eprints.iisc.ernet.in/id/eprint/14935

Actions (login required)

View Item View Item