Phase equilibria and thermodynamic properties of ternary oxides in the system Co-Mo-O

Jacob, KT and Varamban, S Vana (1998) Phase equilibria and thermodynamic properties of ternary oxides in the system Co-Mo-O. In: Journal of Alloys and Compounds, 280 (1-2). pp. 138-146.

[img] PDF
Phase_equilibria_and_thermodynamic.pdf - Published Version
Restricted to Registered users only

Download (364Kb) | Request a copy
Official URL: http://www.sciencedirect.com/science?_ob=ArticleUR...

Abstract

Coexisting phases in the ternary system Co-Mo-O at 1200 K have been identified by X-ray diffraction, optical and scanning electron microscopy and energy dispersive analysis of X-rays. The samples were equilibrated in evacuated quartz capsules and in oxygen gas. Two ternary oxides, Co2Mo3O8 and CoMoO4 were found to be stable. The compound Co2Mo3O8 was found to be in equilibrium with Go-rich metallic solid solutions. Other alloy phases with X-Mo>0.03 and intermetallics were found to be in equilibrium with MoO2. The oxygen chemical potential corresponding to the three-phase fields, CoO+Co2Mo3O8+CoMoO4, MoO2+Co2Mo3O8+CoMoO4 and Co0.97Mo0.03 + MoO2+Co2Mo3O8 were measured using three separate solid state cells incorporating (Y2O3)ZrO2 as the solid electrolyte and a mixture of Co+CoO as the reference electrode. The standard Gibbs energies of formation of the two interoxide compounds from binary oxides CoO and MoO2 (Delta G degrees(f,ox)) were deduced from the emf of the three cells. The high-temperature alpha-modification of CoMoO4 was found to disorder at 1145(+/-5) K. The measurements on all the three cells were internally consistent. The results can be represented by the equations:

Item Type: Journal Article
Additional Information: Copyright of this article belongs to Elsevier Science.
Keywords: Co2Mo3O8;CoMoO4;Gibbs energy;Phase diagram;Chemical potential diagram.
Department/Centre: Division of Chemical Sciences > Materials Research Centre
Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 30 Dec 2009 07:45
Last Modified: 19 Sep 2010 05:26
URI: http://eprints.iisc.ernet.in/id/eprint/19040

Actions (login required)

View Item View Item