Glass forming ability and stability: Ternary Cu bearing Ti, Zr, Hf alloys

Basu, Joysurya and Ranganathan, S (2009) Glass forming ability and stability: Ternary Cu bearing Ti, Zr, Hf alloys. In: Intermetallics, 17 (3). pp. 128-135.

[img] PDF
2.pdf - Published Version
Restricted to Registered users only

Download (704Kb) | Request a copy
Official URL: http://www.sciencedirect.com/science?_ob=ArticleUR...

Abstract

Four Cu bearing alloys of nominal composition Zr25Ti25Cu50, Zr34Ti16Cu50, Zr25Hf25Cu50 and Ti25Hf25Cu50 have been rapidly solidified in order to produce ribbons. All the alloys become amorphous after meltspinning. In the Zr34Ti16Cu50 alloy localized precipitation of cF24 Cu5Zr phase can be observed in the amorphous matrix. The alloys show a tendency of phase separation at the initial stages of crystallization. The difference in crystallization behavior of these alloys with Ni bearing ternary alloys can be explained by atomic size, binary heat of mixing and Mendeleev number. It has been observed that both Laves and Anti-Laves phase forming compositions are suitable for glass formation. The structures of the phases, precipitated during rapid solidification and crystallization can be viewed in terms of Bernal deltahedra and Frank-Kasper polyhedra.

Item Type: Journal Article
Additional Information: Copyright of this article belongs to Elsevier Science.
Keywords: Intermetallics, Laves phases;Metallic glasses;Rapid solidification processing.
Department/Centre: Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 23 Jul 2009 05:01
Last Modified: 19 Sep 2010 05:29
URI: http://eprints.iisc.ernet.in/id/eprint/19566

Actions (login required)

View Item View Item