Dynamic strain ageing in Ni-base superalloy 720Li

Gopinath, K and Gogia, AK and Kamat, SV and Ramamurty, U (2009) Dynamic strain ageing in Ni-base superalloy 720Li. In: Acta Materialia, 57 (4). pp. 1243-1253.

[img] PDF
1.pdf - Published Version
Restricted to Registered users only

Download (1097Kb) | Request a copy
Official URL: http://www.sciencedirect.com/science?_ob=MImg&_ima...

Abstract

An experimental investigation into the dynamic strain ageing (DSA) of a wrought Ni-base superalloy 720Li was conducted. Characteristics of jerky, flow have been studied at intermediate temperatures of 350, 400 and 450 degrees C at strain-rates between 10(-3) and 10(-5) s(-1). Serrations of Type C are predominant within the temperature/strain-rate range explored. The major characteristics of the serrations-i.e. (a) critical plastic strain for onset of serrations, epsilon(c); (b) average stress decrement, Delta sigma(avg); and (c) strain increment between serrations. Delta epsilon(BS)-have been examined at selected temperatures and strain-rates. Negative strain-rate sensitivity was observed in the DSA regime. However. temperature did not influence tensile properties such as yield strength, ultimate strength. elongation, reduction in area, and work hardening rate or fracture features in DSA regime. Analysis of the results Suggests that locking of the mobile dislocations by substitutional alloying elements is responsible for the DSA in alloy 720Li.

Item Type: Journal Article
Additional Information: Copyright of this article belongs to Elsevier Science.
Keywords: 720Li;Jerky flow;Dynamic strain ageing.
Department/Centre: Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 30 Apr 2009 05:10
Last Modified: 19 Sep 2010 05:29
URI: http://eprints.iisc.ernet.in/id/eprint/19700

Actions (login required)

View Item View Item