Pai, BC and Rohatgi, PK and Venkatesha, S (1974) Wear resistance of cast graphitic aluminium alloys. In: Wear, 30 (1). pp. 117-125.
full.pdf - Published Version
Restricted to Registered users only
Download (818Kb) | Request a copy
Wear rates of several cast aluminium base alloys have been measured for lubricated rubbing against a rotating hardened steel disk. Wear rates of cast graphitic aluminium-silicon-nickel alloys were lower than those of pure Al, Al-Si and Al-Si-Ni alloys especially above pressures of 0.02 kg/mm2. The high wear resistance is attributed to the presence of graphite particles in the matrix which act as a solid lubricant. Additions of nickel alone to Al-Si alloys decrease the wear resistance. Graphitic aluminium-silicon-nickel alloys containing above 2% graphite can be mated unlubricated against the rotating steel disk after a one minute lubricated run-in period. Graphite particles may be potentially suitable to replace part of all of the tin in aluminium-tin bearing alloys.
|Item Type:||Journal Article|
|Additional Information:||Copyright of this article belongs to Elsevier Science.|
|Department/Centre:||Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)|
|Date Deposited:||22 Dec 2009 11:11|
|Last Modified:||19 Sep 2010 05:44|
Actions (login required)