Determination of the thermodynamic stability of TiB2

Jain, Ashish and Pankajavalli, R and Anthonysamy, S and Ananthasivan, K and Babu, R and Ganesan, V and Gupta, GS (2010) Determination of the thermodynamic stability of TiB2. In: Journal of Alloys and Compounds, 491 (1-2). pp. 747-752.

[img] PDF
34.pdf - Published Version
Restricted to Registered users only

Download (549Kb) | Request a copy
Official URL: http://www.sciencedirect.com/science?_ob=ArticleUR...

Abstract

The standard free energy of formation of titanium boride (TiB2) Was measured by the Electro Motive Force (EMF) method (by using yttria doped thoria (YDT) as the solid electrolyte). Two galvanic cells viz. Cell (I): Pt, TiB2 (s), TiO2 (s), B (s) vertical bar YDT vertical bar NiO (s), Ni (s), Pt and cell (II): Pt, TiB2 (s), TiO2 (s), B (s) vertical bar YDT vertical bar FeO (s). Fe (s), Pt were constructed in order to determine the Delta(f)G degrees, of TiB2. Enthalpy increments on TiB2 were measured by using inverse drop calorimetry over the temperature range 583-1769 K. The heat capacity, entropy and the free energy function have been derived from these experimental data in the temperature range 298-1800 K. The mean value of the standard enthalpy of formation of TiB2 (Delta H-f(298)degrees (TiB2)) was obtained by combining these Delta(f)G degrees, values and the free energy functions of TiB2 derived from the drop calorimetry data. The mean values of Delta H-f(298)degrees (TiB2) derived from the Delta(f)G degrees, data obtained from cell I and II were -322 +/- 1.2 kJ mol(-1) and -323.3 +/- 2.1 kJ mol(-1), respectively. These values were found to be in very good agreement with the assessed data. (C) 2009 Elsevier B.V. All rights reserved.

Item Type: Journal Article
Additional Information: Copyright of this article belongs to Elsevier Science.
Keywords: Titanium boride; Yttria doped thoria; EMF method; Standard free energy of formation; Enthalpy increment
Department/Centre: Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 29 Mar 2010 11:57
Last Modified: 19 Sep 2010 05:57
URI: http://eprints.iisc.ernet.in/id/eprint/26238

Actions (login required)

View Item View Item