Phase-Field Simulation of Fusion Interface Events during Solidification of Dissimilar Welds: Effect of Composition Inhomogeneity

Chatterjee, Subhradeep and Abinandanan, TA and Chattopadhyay, Kamanio (2008) Phase-Field Simulation of Fusion Interface Events during Solidification of Dissimilar Welds: Effect of Composition Inhomogeneity. In: Symposium on Materials Behavior - Far from Equilibrium, DEC 15-16, 2006, Bombay.

[img] PDF
fulltext1.pdf - Published Version
Restricted to Registered users only

Download (615Kb) | Request a copy
Official URL: http://www.springerlink.com/content/7035433pt61187...

Abstract

We investigate the events near the fusion interfaces of dissimilar welds using a phase-field model developed for single-phase solidification of binary alloys. The parameters used here correspond to the dissimilar welding of a Ni/Cu couple. The events at the Ni and the Cu interface are very different, which illustrate the importance of the phase diagram through the slope of the liquidus curves. In the Ni side, where the liquidus temperature decreases with increasing alloying, solutal melting of the base metal takes place; the resolidification, with continuously increasing solid composition, is very sluggish until the interface encounters a homogeneous melt composition. The growth difficulty of the base metal increases with increasing initial melt composition, which is equivalent to a steeper slope of the liquidus curve. In the Cu side, the initial conditions result in a deeply undercooled melt and contributions from both constrained and unconstrained modes of growth are observed. The simulations bring out the possibility of nucleation of a concentrated solid phase from the melt, and a secondary melting of the substrate due to the associated recalescence event. The results for the Ni and Cu interfaces can be used to understand more complex dissimilar weld interfaces involving multiphase solidification.

Item Type: Conference Paper
Additional Information: Copyright of this article belongs to The Minerals, Metals & Materials Society.
Department/Centre: Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 29 Mar 2010 10:51
Last Modified: 19 Sep 2010 05:58
URI: http://eprints.iisc.ernet.in/id/eprint/26670