Thermal properties of MOSi2 with minor aluminum substitutions

Dasgupta, T and Umarji, AM (2007) Thermal properties of MOSi2 with minor aluminum substitutions. In: Intermetallics, 15 (2). pp. 128-132.

PDF aplctn.pdf - Published Version Restricted to Registered users only Download (301Kb) | Request a copy

Abstract

Mo(Si1-xAlx)(2) compositions (x = 0-0.1) have been prepared by a modified SHS route under uniaxial hydrostatic pressure. Oxidation studies carried out by thermal analysis and sheet resistivity indicate an improvement in the low temperature (700-900 K) oxidation resistance with increasing aluminum addition. Dilatometric results show a decrease in the a value up to x = 0.05 substitution. With the aluminum substitution, both thermal expansion coefficient and thermal conductivity show decrease in their values except in the biphasic region. The x = 0.05 composition containing both C11(b) and C40 phases is a promising material for high temperature thermal barrier coating as it shows higher oxidation resistance and a similar K/alpha value as compared to pure MoSi, (c) 2006 Elsevier Ltd. All rights reserved.

Item Type:	Journal Article
Additional Information:	Copyright of this article belongs to Elsevier Science.
Department/Centre:	Division of Chemical Sciences > Materials Research Centre
Date Deposited:	10 Jun 2010 05:03
Last Modified:	19 Sep 2010 05:59
URI:	http://eprints.iisc.ernet.in/id/eprint/26886

Actions (login required)

View Item