Effect of densification and TiB2 reinforcement on the wear of molybdenum disilicide

Ramasesha, Sheela K and Srikari, Tantri P and Jayasingh, Moses E and Biswas, SK (2000) Effect of densification and TiB2 reinforcement on the wear of molybdenum disilicide. In: Tribology Letters, 8 (4). pp. 219-222.

[img] PDF
wear.pdf - Published Version
Restricted to Registered users only

Download (111Kb) | Request a copy
Official URL: http://www.springerlink.com/content/w8v98524g6v422...

Abstract

Wear tests were done in a pin-on-disc machine by sliding MoSi2 pins against hard-steel discs in a normal load range of 5-140 N and a speed of 0.5 m/s under nominally dry conditions in the ambient. The specific wear rate of the pin undergoes two transitions: severe to mild at low load and mild to severe at high load. The mild-wear domain is distinguished by the formation of a protective mechanically mixed layer of steel and its oxides, transferred from the counterface in particulate form. Increasing the hardness by densification and TiB2 reinforcement lowers the specific wear rate and expands the mild-wear load domain. However, even when the volume wear rate is normalised with respect to the real contact area (load/hardness) the non-dimensional wear factor is still seen to decrease with densification and reinforcement. This indicates that fracture toughness may also play an important role in determining the wear-resistance of these materials. The surface coverage on the pin by the mechanically mixed layer increases with densification and reinforcement.

Item Type: Journal Article
Additional Information: Copyright of this article belongs to Springer.
Keywords: wear;molybdenum disilicide;densification;reinforcement; hardness;fracture toughness.
Department/Centre: Division of Mechanical Sciences > Mechanical Engineering
Date Deposited: 04 Aug 2010 09:00
Last Modified: 19 Sep 2010 06:13
URI: http://eprints.iisc.ernet.in/id/eprint/31063

Actions (login required)

View Item View Item