Jacob, KT and Srikanth , S (1988) Use of metastable equilibria for determination of Gibbs energy of solids. In: Journal of Materials Research, 3 (4). 687 -693.
Use_of_metastable_equilibria.pdf - Published Version
Restricted to Registered users only
Download (586Kb) | Request a copy
Attempts are made to measure activities of both components of a binary alloy (Aï¿½B) at 650 K using a solid-state galvanic cell incorporating a new composite solid electrolyte. Since the ionic conductivity of the composite solid electrolyte is three orders of magnitude higher than that of pure CaF2, the cell can be operated at lower temperatures. The alloy phase is equilibrated in separate experiments with flourides of each component and fluorine potential is measured. The mixture of the alloy (Aï¿½B) and the fluoride of the more reactive component (BF2) is stable, while (Aï¿½B) + AF2 mixture is metastable, Factors governing the possible use of metastable equilibria have been elucidated in this study. In the Coï¿½Ni system, where the difference in Gibbs energies of formation of the fluorides is 21.4 kJ/mol, emf of the cell with metastable phases at the electrode is constant for periods ranging from 90 to 160 ks depending on alloy composition. Subsequently, the emf decreases because of the onset of the displacement reaction. In the Niï¿½Mn system, measurement of the activity of Ni using metastable equilibria is not fully successful at 650 K because of the large driving force for the displacement reaction (208.8 kJ/mol). Critical factors in the application of metastable equilibria are the driving force for displacement reaction and diffusion coefficients in both the alloy and fluoride solid solution.
|Item Type:||Journal Article|
|Additional Information:||Copyright of this article belongs to The Materials Research Society.|
|Department/Centre:||Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)|
|Date Deposited:||13 Oct 2010 09:37|
|Last Modified:||13 Oct 2010 09:37|
Actions (login required)