Chandrasekaran, T and Natarajan, KA and Kishore, * (1991) Influence of microstructure on the wear of grinding media. In: Wear, 147 (2). 267 -274.
Influence_of_microstructure_on.pdf - Published Version
Restricted to Registered users only
Download (1500Kb) | Request a copy
Owing to the complexity of the wear process, high stress grinding abrasion is quite different from two-body abrasive wear. Reported data on two-body abrasive wear reveal that the wear decreases with an increase in steel hardness. This relationship can be established without having to consider the microstructure of the steel grinding medium. However, it is known that hardness cannot be directly employed to predict the wear of steel balls under three-body grinding abrasion, as occurs during dry grinding of ores in ball mills. The present work suggests that the wear behaviour of grinding balls can be classified according to the microstructural family to which they belong. Thus, in this work on AISI 52100 steel, the separate groups of microstructures were spheroidite—pearlite, bainite, tempered martensite and martensite with retained austenite. It appears that wear behaviour of the first three groups follows the same trend as that observed for two-body wear. The data suggest that an optimum level of retained austenite could improve the wear resistance of microstructures containing martensite.
|Item Type:||Journal Article|
|Additional Information:||Copyright of this article belongs to Elsevier science.|
|Department/Centre:||Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)|
|Date Deposited:||18 Nov 2010 10:23|
|Last Modified:||18 Nov 2010 10:23|
Actions (login required)