Suhail, MH and Mohan, Rao G and Mohan, S (1992) dc reactive magnetron sputtering of titanium‐structural and optical characterization of TiO2 films. In: Journal of Applied Physics, 71 (3). pp. 1421-1427.
dc.pdf - Published Version
Restricted to Registered users only
Download (745Kb) | Request a copy
This paper deals with the reactive sputtering of titanium in an argon and oxygen mixture. The variation in cathode potential as a function of oxygen partial pressure has been explained in terms of cathode poisoning effects. The titania films deposited during this process have been studied for their structural and optical characteristics. The effect of substrate temperature (from 25 to 400 °C) and annealing (from 250 to 700 °C) on the packing density, refractive index, extinction coefficient, and crystallinity has been investigated. The refractive index varied from 2.24 to 2.46 and extinction coefficient from 2.6 × 10-3 to 10.4× 10-3 at 500 nm as the substrate temperature increased from 25 to 400 °C. The refractive index increased from 2.19 to 2.35 and extinction coefficient changed from 3.2× 10-3 to 11.6 × 10-3 at 500 nm as the annealing temperature was increased from 250 to 700 °C. Anatase and rutile phases have been observed in the films deposited at 400 °C substrate temperature and annealed at 300 °C. The changes in the optical constants at higher substrate temperature have been attributed to an increase in packing density, oxygen content, and crystallinity of the films.
|Item Type:||Journal Article|
|Additional Information:||Copyright of this article belongs to American Institute of Physics.|
|Department/Centre:||Division of Physical & Mathematical Sciences > Instrumentation and Applied Physics (Formally ISU)|
|Date Deposited:||25 Jan 2011 05:09|
|Last Modified:||25 Jan 2011 05:09|
Actions (login required)