Effect of zinc content on the processing map for hot working of α brass

Padmavardhani, D and Prasad, YVRK (1992) Effect of zinc content on the processing map for hot working of α brass. In: Materials Science and Engineering: A, 157 (1). pp. 43-51.

[img] PDF
Effect_of_zinc_content.pdf - Published Version
Restricted to Registered users only

Download (670Kb) | Request a copy
Official URL: http://dx.doi.org/10.1016/0921-5093(92)90097-K

Abstract

The hot deformation behavior of α brass with varying zinc contents in the range 3%–30% was characterized using hot compression testing in the temperature range 600–900 °C and strain rate range 0.001–100 s−1. On the basis of the flow stress data, processing maps showing the variation of the efficiency of power dissipation (given by Image where m is the strain rate sensitivity) with temperature and strain rate were obtained. α brass exhibits a domain of dynamic recrystallization (DRX) at temperatures greater than 0.85Tm and at strain rates lower than 1 s−1. The maximum efficiency of power dissipation increases with increasing zinc content and is in the range 33%–53%. The DRX domain shifts to lower strain rates for higher zinc contents and the strain rate for peak efficiency is in the range 0.0001–0.05 s−1. The results indicate that the DRX in α brass is controlled by the rate of interface formation (nucleation) which depends on the diffusion-controlled process of thermal recovery by climb.

Item Type: Journal Article
Additional Information: Copyright of this article belongs to Elsevier science.
Department/Centre: Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 24 Jan 2011 10:28
Last Modified: 24 Jan 2011 10:28
URI: http://eprints.iisc.ernet.in/id/eprint/35205

Actions (login required)

View Item View Item