Intercalation of n-alkylamines in iron thiohypophosphate (FePS3)

Joy, Pattayil Alias and Vasudevan, Sukumaran (1993) Intercalation of n-alkylamines in iron thiohypophosphate (FePS3). In: Chemistry of Materials, 5 (8). pp. 1182-1191.

[img] PDF
Alkyla.pdf - Published Version
Restricted to Registered users only

Download (1216Kb) | Request a copy
Official URL: http://pubs.acs.org/doi/abs/10.1021/cm00032a024

Abstract

The intercalation of linear alkylamines (C1-C4) in the two-dimensional (2D) Ising antiferromagnet, FePS3, has been investigated. Intercalation proceeds with a dilation of the interlayer distance. The expansion (approximately 3.8 angstrom) is the same for all four amine molecules, suggesting that they are oriented flat with respect to the layers. From an analysis of the products of deintercalation, it is concluded that the intercalated species are the alkylammonium cations and neutral amine molecules. The intercalated compounds are highly moisture sensitive, as reflected in the chemical nature of the intercalated species. Charge neutrality of the lattice after intercalation is preserved by the loss of Fe2+ ions from the lattice. These Fe2+ ions are further oxidized to form superparamagnetic Fe2O3 clusters, as confirmed by Mossbauer spectra and magnetic measurements. This was further corroborated by in situ EPR studies. The Fe-57 Mossbauer spectra of the intercalated compounds showed evidence for two species other than Fe2O3. On the basis of the observed isomer shifts and quadrupole splittings, they have been assigned to Fe2+ in an environment similar to that in FePS3 and in a distorted FePS3 environment. The temperature and field dependence of the magnetic susceptibility of single crystals of the amine-intercalated FePS3 have been measured. Their magnetic behavior shows many of the features expected of a 2D Ising antiferromagnet with random defects, Fe1-xPS3, in agreement with the mechanism of intercalation.

Item Type: Journal Article
Additional Information: Copyright of this article belongs to American Chemical Society.
Department/Centre: Division of Chemical Sciences > Inorganic & Physical Chemistry
Date Deposited: 10 Feb 2011 10:38
Last Modified: 10 Feb 2011 10:38
URI: http://eprints.iisc.ernet.in/id/eprint/35512

Actions (login required)

View Item View Item