Jacob, KT and Waseda, Y (1994) Gibbs energy of formation of orthorhombic CaZrO3. In: Thermochimica acta, 239 . 233 -241 .
GIBBS_ENERGY.pdf - Published Version
Restricted to Registered users only
Download (603Kb) | Request a copy
The Gibbs free energy of formation of the orthorhombic form of CaZrO3(o) from monoclinic ZrO2(m) and periclase CaO(p) has been determined as a function of temperature in the range 950-1225 K, using an electrochemical cell incorporating single-crystal CaF2 as the solid electrolyte. The results are corrected for the small solid solubility of CaO in ZrO2. For the reaction, ZrO2(m) + CaO(p) --> CaZrO3(o), DELTAG(phi) = -31590 -13.9T(+/- 180) J mol-1. The ''second-law'' enthalpy of formation of CaZrO3 obtained from the results of this study at a mean temperature of 1090 K is in excellent agreement with the high-temperature solution calorimetric measurements of Muromachi and Navrotsky at 1068 K (J. Solid State Chem., 72 (1988) 244), and the average value of the bomb and acid solution calorimetric studies of Lvova and Feodosev (Zh. Fiz. Khim., 38 (1964) 28), Korneev et al. (Izv. Akad. Nauk SSSR, Neorg. Mater., 7 (1971) 886) and Brown and Bennington (Thermochim. Acta, 106 (1986) 183). The standard entropy of CaZrO3(o) at 298.15 K from the free energy data is 96.4 (+/- 3.5) J K-1 mol-1. The results of this study are discussed in comparison with high-temperture e.m.f. measurements reported in the literature on cubic zirconia solid solutions.
|Item Type:||Journal Article|
|Additional Information:||Copyright of this article belongs to Elsevier Science.|
|Department/Centre:||Division of Chemical Sciences > Materials Research Centre|
|Date Deposited:||24 May 2011 09:20|
|Last Modified:||24 May 2011 09:20|
Actions (login required)