Phase relations and gibbs energies in the system Mn-Rh-O

Jacob, KT and Sriram, MV (1994) Phase relations and gibbs energies in the system Mn-Rh-O. In: Metallurgical and Materials Transactions A, 25 (7). pp. 1347-1357.

[img] PDF
Phase_Relations.pdf - Published Version
Restricted to Registered users only

Download (1053Kb) | Request a copy
Official URL: http://www.springerlink.com/content/0n3316328462wp...

Abstract

Phase relations in the system Mn-Rh-O are established at 1273 K by equilibrating different compositions either in evacuated quartz ampules or in pure oxygen at a pressure of 1.01 x 10(5) Pa. The quenched samples are examined by optical microscopy, X-ray diffraction, and energy-dispersive X-ray analysis (EDAX). The alloys and intermetallics in the binary Mn-Rh system are found to be in equilibrium with MnO. There is only one ternary compound, MnRh2O4, with normal spinel structure in the system. The compound Mn3O4 has a tetragonal structure at 1273 K. A solid solution is formed between MnRh2O4 and Mn3O4. The solid solution has the cubic structure over a large range of composition and coexists with metallic rhodium. The partial pressure of oxygen corresponding to this two-phase equilibrium is measured as a function of the composition of the spinel solid solution and temperature. A new solid-state cell, with three separate electrode compartments, is designed to measure accurately the chemical potential of oxygen in the two-phase mixture, Rh + Mn3-2xRh2xO4, which has 1 degree of freedom at constant temperature. From the electromotive force (emf), thermodynamic mixing properties of the Mn3O4-MnRh2O4 solid solution and Gibbs energy of formation of MnRh2O4 are deduced. The activities exhibit negative deviations from Raoult's law for most of the composition range, except near Mn3O4, where a two-phase region exists. In the cubic phase, the entropy of mixing of the two Rh3+ and Mn3+ ions on the octahedral site of the spinel is ideal, and the enthalpy of mixing is positive and symmetric with respect to composition. For the formation of the spinel (sp) from component oxides with rock salt (rs) and orthorhombic (orth) structures according to the reaction, MnO (rs) + Rh2O3 (orth) --> MnRh2O4 (sp), DELTAG-degrees = -49,680 + 1.56T (+/-500) J mol-1. The oxygen potentials corresponding to MnO + Mn3O4 and Rh + Rh2O3 equilibria are also obtained from potentiometric measurements on galvanic cells incorporating yttria-stabilized zirconia as the solid electrolyte. From these results, an oxygen potential diagram for the ternary system is developed.

Item Type: Journal Article
Additional Information: Copyright of this article belongs to The minerals, metals & materials society.
Department/Centre: Division of Chemical Sciences > Materials Research Centre
Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 08 Apr 2011 10:17
Last Modified: 08 Apr 2011 10:17
URI: http://eprints.iisc.ernet.in/id/eprint/36685

Actions (login required)

View Item View Item