Phase equilibria in the system CaO-CoO-SiO2 and Gibbs energies of formation of the quaternary oxides CaCoSi2O6, Ca2CoSi2O7, and CaCoSiO4

Mukhopadhyay, Sukanya and Jacob, KT (1996) Phase equilibria in the system CaO-CoO-SiO2 and Gibbs energies of formation of the quaternary oxides CaCoSi2O6, Ca2CoSi2O7, and CaCoSiO4. In: American Mineralogist, 81 (7-8). 963-972 .

[img] PDF
Phase_equilibria.pdf - Published Version
Restricted to Registered users only

Download (1517Kb) | Request a copy
Official URL: http://ammin.geoscienceworld.org/cgi/content/abstr...

Abstract

Phase relations in the pseudoternary system CaO-CoO-SiO2 have been established at 1323 K. Three quaternary oxides were found to be stable: CaCoSi2O6 with clinopyroxene (Cpx), Ca2CoSi2O7 with melilite (Mel), and CaCoSiO4 with olivine (Ol) structures. The Gibbs energies of formation of the quaternary oxides from their component binary oxides were measured using solid-state galvanic cells incorporating yttria-stabilized zirconia as the solid electrolyte in the temperature range of 1000-1324 K. The results can be summarized as follows: CoO (rs) + CaO (rs) + 2SiO(2) (Qtz) --> CaCoSi2O6 (Cpx), Delta G(f)(0) = -117920 + 11.26T (+/-150) J/mol CoO (rs) + 2CaO (rs) + 2SiO(2) (Qtz) --> Ca2CoSi2O7 (Mel), Delta G(f)(0) = -192690 + 2.38T (+/-130) J/mol CoO (rs) + CaO (rs) + SiO2 (Qtz) --> CaCoSiO2 (Ol), Delta G(f)(0) = -100325 + 2.55T (+/-100) J/mol where rs = rock salt (NaCl) structure and Qtz = quartz. The uncertainty limits correspond to twice the standard error estimate. The experimentally observed miscibility gaps along the joins CaO-CoO and CaCoSiO4-Co2SiO4 were used to calculate the excess free energies of mixing for the solid solutions CaxCo1-xO and (CayCo1-y)CoSiO4:Delta G(E) = X(1 - X)[31975X + 26736 (1 - X)] J/mol and Delta G(E) = 23100 (+/-250) Y(1 - Y) J/mol. A T-X phase diagram for the binary CaO-CoO was computed from the thermodynamic information; the diagram agrees with information available in the literature. The computed miscibility gap along the CaCoSiO4-Co2SiO4 join is associated with a critical temperature of 1389 (+/-15) K. Stability fields for the various solid solutions and the quaternary compounds are depicted on chemical-potential diagrams for SiO2, CaO, and CoO at 1323 K.

Item Type: Journal Article
Additional Information: Copyright of this article belongs to Mineralogical Society of America.
Department/Centre: Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 09 May 2011 10:53
Last Modified: 09 May 2011 11:10
URI: http://eprints.iisc.ernet.in/id/eprint/37465

Actions (login required)

View Item View Item