Gandhi, AS and Jayaram, V and Chokshi, AH (1997) Phase evolution and densification of spray pyrolysed ZrO2-Al2O3 powders. In: Materials Science Forum, 243 . 227-232 .
Full text not available from this repository.Abstract
Devitrification of spray pyrolysed, amorphous ZrO2-Al2O3 solid solution produces nanocrystalline microstructures (grain sizes 10-20 nm). In this study, spray pyrolysed amorphous ZrO2-40 mol% Al2O3 powder displayed good sinterability during decomposition, after spraying, of the nitrate precursors up to 1023K. Hot pressing of fully pyrolysed, pre-sintered (more than 70% dense) pellets at 923K and 750 MPa produced an amorphous pellet with less than 2% porosity. The results indicate the possibility of producing dense, amorphous pellets that can be heat treated further to produce nanocrystalline microstructures conducive for superplasticity.
| Item Type: | Editorials/Short Communications |
|---|---|
| Additional Information: | Copyright of this article belongs to Trans Tech Publications Inc. |
| Department/Centre: | Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy) |
| Date Deposited: | 02 Jul 2011 06:52 |
| Last Modified: | 02 Jul 2011 06:52 |
| URI: | http://eprints.iisc.ernet.in/id/eprint/38351 |
Actions (login required)
 |
View Item |