Chinnasamy, CN and Narayanasamy, A and Chattopadhyay, K and Ponpandian, N (1999) Magnetic properties of mechanically alloyed nanocrystalline Ni3Fe. In: Nanostructured Materials, 12 (5-8). pp. 951-954.
MAtGNETIC_PROPERTIES_OF.pdf - Published Version
Restricted to Registered users only
Download (242Kb) | Request a copy
Disordered nanocrystalline Ni3Fe alloy was prepared by mechanical alloying of elemental powders. X-ray diffractograms show the formation of Ni3Fe single phase. The chemical composition and morphology of the powder have been obtained by using EDAX and SEM analysis respectively. While the saturation magnetisation decreases with milling time, the coercivity increases. The width of the hyperfine field distributions obtained from Mossbauer studies shows that the alloy is highly disordered Atomic ordering is found to take place at a faster rate compared to that in the bulk alloy. (C) 1999 Acta Metallurgica Inc.
|Item Type:||Journal Article|
|Additional Information:||Copyright of this article belongs to Elsevier Science.|
|Department/Centre:||Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)|
|Date Deposited:||23 Jun 2011 09:32|
|Last Modified:||23 Jun 2011 09:32|
Actions (login required)