Balam, SSK and Dong, HQ and Laurila, T and Vuorinen, V and Paul, A (2011) Diffusion and Growth of the mu Phase (Ni6Nb7) in the Ni-Nb System. In: Metallurgical and Materials Transactions A, 42A (7). pp. 1727-1731.
Diffusion_and_Growth.pdf - Published Version
Restricted to Registered users only
Download (423Kb) | Request a copy
Incremental diffusion couple experiments are conducted to determine the average interdiffusion coefficient and the intrinsic diffusion coefficients of the species in the Ni6Nb7 (mu phase) in the Ni-Nb system. Further, the tracer diffusion coefficients are calculated from the knowledge of thermodynamic parameters. The diffusion rate of Ni is found to be higher than that of Nb, which indicates higher defect concentration in the Ni sublattice.
|Item Type:||Journal Article|
|Additional Information:||Copyright of this article belongs to Springer.|
|Department/Centre:||Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)|
|Date Deposited:||04 Jul 2011 07:59|
|Last Modified:||04 Jul 2011 07:59|
Actions (login required)