Bhatia, Tania and Chattopadhyay, K and Jayaram, Vikram (1999) Segregation in the MgO–MgAl2O4 system processed from nitrate precursors. In: Journal of Materials Research, 14 (8). pp. 3319-3327.Full text not available from this repository.
The occurrence of segregation and its influence on microstructural and phase evolution have been studied in MgO–MgAl2O4 powders synthesized by thermal decomposition of aqueous nitrate precursors. When the nitrate solutions of Mg and Al were spray-pyrolyzed on a substrate held at 673 or 573 K, homogeneous mixed oxides were produced. Spraying and drying the nitrate solutions at 473 K resulted in the formation of compositionally inhomogeneous, segregated oxide mixtures. It is suggested that segregation in the dried powders was caused by the difference in solubility of the individual nitrate salts in water which caused Mg-rich and Al-rich salts to precipitate during dehydration of the solutions. The occurrence of segregation in the powders sprayed at 473 K and not 573 or 673 K is ascribed to the sluggish rate at which the early stages of decomposition occurred during which the cations segregated. The phase evolution in segregated and segregation-free MgO–MgAl2O4 powders has been compared. The distinguishing feature of the segregated powders was the appearance of stoichiometric periclase grain dimensions in excess of 0.3 μm at temperatures as low as 973 K. By comparison, the segregation-free powders displayed broad diffraction peaks corresponding to fine-grained and nonstoichiometric periclase. The grain size was in the range 5–30 nm at temperatures up to 1173 K. The key to obtaining fine-grained periclase was the ability to synthesize (Mg Al)O solid solutions with the rock salt structure. In the temperature range 973–1173 K, spinel grain size varied from 5 to 40 nm irrespective of its composition and did not appear to be influenced by segregation.
|Item Type:||Journal Article|
|Additional Information:||Copyright of this article belongs to Cambridge University Press.|
|Department/Centre:||Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)|
|Date Deposited:||11 Aug 2011 13:14|
|Last Modified:||11 Aug 2011 13:14|
Actions (login required)