Chattopadhyay, K and Biswas, K and Bysakh, S and Phanikumar, G and Weisheit, A and Galun, R and Mordike, B (2000) Quasicrystalline Coatings Through Laser Processing: A Study on Process Optimisation and Microstructure Evolution. In: MRS Proceedings, 643 .Full text not available from this repository.
Composite coatings containing quasicrystalline (QC) phases in Al-Cu-Fe alloys were prepared by laser cladding using a mixture of the elemental powders. Two substrates, namely pure aluminum and an Al-Si alloy were used. The clad layers were remelted at different scanning velocities to alter the growth conditions of different phases. The process parameters were optimized to produce quasicrystalline phases. The evolution of the microstructure in the coating layer was characterized by detailed microstructural investigation. The results indicate presence of quasicrystals in the aluminum substrate. However, only approximant phase could be observed in the substrate of Al-Si alloys. It is shown that there is a significant transport of Si atoms from the substrate to the clad layer during the cladding and remelting process. The hardness profiles of coatings on aluminum substrate indicate a very high hardness. The coating on Al-Si alloy, on the other hand, is ductile and soft. The fracture toughness of the hard coating on aluminum was obtained by nano-indentation technique. The K1C value was found to be 1.33 MPa m1/2 which is typical of brittle materials.
|Item Type:||Journal Article|
|Additional Information:||Copyright of this article belongs to Cambridge University Press.|
|Department/Centre:||Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)|
|Date Deposited:||17 Aug 2011 09:20|
|Last Modified:||17 Aug 2011 09:20|
Actions (login required)