Tie lines and activities in the system CoO MgO SiO2 at 1373 K

Jacob, KT and Mukhopadhyay, Sukanya and Shukla, AK (1992) Tie lines and activities in the system CoO MgO SiO2 at 1373 K. In: Journal of the American Ceramic Society, 75 (11). pp. 3081-3086.

[img] PDF
196._CoO-MgO-SiO2._JACS._1992.pdf - Published Version
Restricted to Registered users only

Download (552Kb) | Request a copy
Official URL: http://onlinelibrary.wiley.com/doi/10.1111/j.1151-...

Abstract

The tie lines between (CoXMg1−X)O solid solution with rock salt structure and orthosilicate solid solution (CoYMg1−Y)-Si0.5O2, and between orthosilicate and metasilicate (CoZMg1-Z)SiO3 crystalline solutions, have been determined experimentally at 1373 K. The compositions of coexisting phases have been determined by electron probe microanalysis (EPMA) and lattice parameter measurement on equilibrated samples. The metasilicate solid solution exists only for 0 > Z > 0.213. The activity of CoO in the rock salt solid solution was determined as a function of composition and temperature in the range of 1023 to 1373 K using a solid-state galvanic cell: Pt, (CoXMg1−X)O+Co|(Y2O3)ZrO2|Co+CoO, Pt The free energy of mixing of (CoXMg1−X)O crystalline solution can be expressed by the equation ΔGE=X(1 −X)[(6048 − 2.146T)X+ (8745 − 3.09T)(1 −X)] J·mol−1 The thermodynamic data for the rock salt phase is combined with information on interphase partitioning of Co and Mg to generate the mixing properties for the ortho- and metasilicate solid solutions. For the orthosilicate solution (CoYMg1 −Y)Si0.5O2 at 1373 K, the excess Gibbs free energy of mixing is given by the relation ΔGE=Y(1 −Y)[2805Y+ 3261(1 −Y)] J·mol−1 For the metasilicate solution (CoZMg1 −Z)SiO3 at the same temperature, the excess free energy can be expressed by the relation ΔGE=Z(1 −Z)[2570Z+ 3627(1 −Z)] J·mol−1

Item Type: Journal Article
Additional Information: Copyright of this article belongs to John Wiley and Sons.
Department/Centre: Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 09 Dec 2011 09:14
Last Modified: 09 Dec 2011 09:18
URI: http://eprints.iisc.ernet.in/id/eprint/42681

Actions (login required)

View Item View Item