Effect of Grain Size on Structural and Magnetic Properties of CuFe2O4 Nanograins Synthesized by Chemical Co-Precipitation

Hoque, S Manjura and Kader, SS and Paul, DP and Saha, DK and Das, HN and Rana, MS and Chattopadhyay, K and Hakim, MA (2012) Effect of Grain Size on Structural and Magnetic Properties of CuFe2O4 Nanograins Synthesized by Chemical Co-Precipitation. In: IEEE TRANSACTIONS ON MAGNETICS, 48 (5, Par). pp. 1839-1843.

[img] PDF
IEE_tran_on_mag_48_5_1839-1843_2012.pdf - Published Version
Restricted to Registered users only

Download (397Kb) | Request a copy
Official URL: http://dx.doi.org/10.1109/TMAG.2011.2173207

Abstract

CuFe2O4 nanograins have been prepared by the chemical co-precipitation technique and calcined in the temperature range of 200-1200 degrees C for 3 h. A wide range of grain sizes has been observed in this sintering temperature range, which has been determined to be 4 to 56 nm. Formation of ferrite has also been confirmed by FTIR measurement through the presence of wide band near 600 and 430 cm(-1) for the samples in the as-dried condition. Systematic variation of wave number has been observed with the variation of the calcination temperature. B-H loops exhibit transition from superparamagnetic to ferrimagnetic state above the calcination temperature of 900 degrees C. Coercivity of the samples at lower calcination temperature of 900 degrees C reduces significantly and tends towards zero coercivity, which is suggestive of superparamagnetic transition for the samples sintered below this temperature. Frequency spectrum of the real and imaginary part of complex initial permeability have been measured for the samples calcined at different temperature, which shows wide range of frequency stability. Curie temperature, T-c has been measured from temperature dependence initial permeability at a fixed frequency of 100 kHz. Although there is small variation of T-c with sintering temperature, the reduction of permeability with temperature drastically reduce for lower sintering temperature, which is in conformity with the change of B-H loops with the variation of sintering temperatures.

Item Type: Journal Article
Keywords: Coercivity , CuFe$_{2}$O $_{4}$ , Neél temperature , initial permeability
Department/Centre: Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 16 Jul 2012 10:00
Last Modified: 16 Jul 2012 10:00
URI: http://eprints.iisc.ernet.in/id/eprint/44590

Actions (login required)

View Item View Item