Fretting wear study of Cu-10 wt% TiB2 and Cu-10 wt% TiB2-10 wt% Pb composites

Sharma, Amit S and Mishra, Nisha and Biswas, Krishanu and Basu, Bikramjit (2013) Fretting wear study of Cu-10 wt% TiB2 and Cu-10 wt% TiB2-10 wt% Pb composites. In: WEAR, 306 (1-2). pp. 138-148.

[img] PDF
Wear_306-1-2_138_2013.pdf - Published Version
Restricted to Registered users only

Download (4MB) | Request a copy
Official URL: http://dx.doi.org/10.1016/j.wear.2013.07.009

Abstract

In developing materials with better tribological properties, it is always conceived that the addition of softer phase would result in better frictional behavior. In order to address this issue, we report here the results of fretting wear study on Cu-10 wt% TiB2 and Cu-10 wt% TiB2-10 wt% Pb composites, sintered using spark plasma sintering (SPS) technique. It was found out that the addition of softer phase i.e. 10 wt % Pb to Cu-10 wt% TiB2 composites has not resulted in the lowering of the coefficient of friction (COF). The combination of steady state COF (0.6) and wear rate (10(-3) mm(3)/N-m) was measured and such properties are even better than that obtained with TiB2 coatings reported in the literature. For Cu-10 wt% TiB2 sintered at different temperature, a lower wear resistance with increase in hardness is being measured. An attempt has been made to correlate the observed wear behavior with the surface and subsurface deformation. The formation of a wear-resistant delaminated tribolayer consisting of TiB2 particles and ultrafine oxide debris (Cu, Fe, Ti)(x)O-y was the reason assigned for the observed low wear rate of these composites. (C) 2013 Elsevier B.V. All rights reserved.

Item Type: Journal Article
Additional Information: copyright for this article belongs to ELSEVIER SCIENCE SA, SWITZERLAND
Keywords: Fretting; Hardness; Metal-matrix composite; Bearings; Profilometry
Department/Centre: Division of Chemical Sciences > Materials Research Centre
Depositing User: Id for Latest eprints
Date Deposited: 24 Jan 2014 07:12
Last Modified: 24 Jan 2014 07:12
URI: http://eprints.iisc.ac.in/id/eprint/48228

Actions (login required)

View Item View Item