Influence of precipitation on serrated flow in Al – 5Zn–1Mg alloy

Kumar, S and Shabadi, R and Patel, MM (2003) Influence of precipitation on serrated flow in Al – 5Zn–1Mg alloy. In: Materials Science and Technology, 19 (10). pp. 1344-1348.

[img] PDF
Influence_of_precipitation.pdf
Restricted to Registered users only

Download (243Kb) | Request a copy

Abstract

An Al – 5Zn – 1Mg alloy was aged at three different temperatures, 70°C, 150°C, and 200°C to obtain different states of precipitation. Serrated flow behaviour was studied with progressive aging at these three different aging temperatures. A comparison of serrated flow behaviour for the three different aging condition was made in the peak aged condition. Finally, serrated flow behaviour in Al – 5Zn – 1Mg alloy was compared with that in Al – Li alloys studied earlier. It is concluded that all the features of serrated flow can be explained only by considering the combined effect of solute – dislocation and precipitate – dislocation interaction.

Item Type: Journal Article
Additional Information: The Copyright belongs to IoM Communications Ltd.
Department/Centre: Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 03 May 2006
Last Modified: 19 Sep 2010 04:26
URI: http://eprints.iisc.ernet.in/id/eprint/6543

Actions (login required)

View Item View Item